Abstract
|
Robust superhydrophobic ZnO surfaces with micro/nano hybrid hierarchical structures were synthesized on the stainless steel mesh by a facile single-step chemical bath deposition (CBD) method without using further low surface energy materials. The Taguchi L16 experimental design was applied to evaluate the effects of reaction time, type and concentration of the additive, type of the chelating agent, and the molar ratio of the chelating agent to the initial zinc (II) ions. The prepared sample at the optimal conditions exhibited a sustainable and time-independent superhydrophobic behavior with the water contact angle (WCA) of 162.8° ± 2.5° and contact angle hysteresis (CAH) of 1.8° ± 0.5°. The XRD, SEM, TEM and FTIR analyses were used to characterize the prepared samples. Surface characterization using scanning electron microscopy (SEM) indicated accumulation of micro/nano branched ZnO needles on the substrate with the average diameters of ∼85 nm. After 20 abrasion cycles the optimum sample indicated an excellent mechanical robustness via exposure to the pressure of 4.7 kPa. A suitable chemical resistance to the acidic and basic droplets with the pH range of 4 and 9 was observed.
|